I-alloy esekelwe kwi-nickel luhlobo olukhethekileyo lwe-alloy equkethe i-nickel, ngelixa i-doping encinci yezinye izinto, ezifana nentsimbi, i-chromium, i-manganese njalo njalo.Le alloy inokumelana ne-corrosion kunye namandla aphezulu obushushu.I-nickel-based alloy powder yimathiriyeli yomgubo ocolekileyo eyenziwe ngamasuntswana alloy asekwe kwi-nickel.Xa kuthelekiswa nomgubo wesinyithi wesintu, i-nickel-based alloy powders inokumelana ne-corrosion ephezulu kunye neempawu zobushushu obuphezulu.Ngethuba lenkqubo yokuvelisa, la maqhekeza ancibilika kakuhle kwaye aphantsi ukuqinisekisa iimpawu zabo ezintle zomzimba kunye neekhemikhali.I-powder esekelwe kwi-nickel ineendlela ezininzi zokusetyenziswa kwaye ingasetyenziselwa ukuvelisa amacandelo aphezulu kunye nezixhobo zokwakha.
Into | Iteknoloji | Phula | Ukuxinana | Ukuqina | Ubungakanani | Umxholo | Usetyenziso |
I-HRNi20A | Igesi atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 18-22HRC | -106+45um -90+45um | C:0.1 IsiKr:4.5 Si:2.0 B:0.7 Mna: Bal. | Isitshizi somlilo / ukudibanisa, ukungunda kweglasi, ukuphosa okuhlukeneyo kuyafa. |
I-HRNi22A | Igesi atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 20-24HRC | -106+45um -90+45um | C:0.2 Cr:1.0 Si:2.8 B:1.4 Fe:1.0 Mnu:0.1 Mna: Bal. | Isitshizi somlilo/ukudibanisa ukungunda kweglasi, ukuphosa okwahlukeneyo kuyafa. |
HRNi25 | Igesi atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 22-27HRC | -106+45um -90+45um | C:0.2 Cr:1.0 Si:3.5 B:1.5 Fe:8.0 Mna: Bal. | Isitshizi somlilo/ukudibanisa ukungunda kweglasi, ukuphosa okwahlukeneyo kuyafa. |
I-HRNi28A | Igesi atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 26-30HRC | -106+45um -90+45um | C:0.1 Cr:3.0 Si:2.6 B:1.0 Mna: Bal. | Isitshizi somlilo/ukudibanisa ukungunda kweglasi, ukuphosa okwahlukeneyo kuyafa. |
HRNi35 | Igesi atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 32-37HRC | -106+45um -90+45um | C:0.3 IKr:10 Si:3.5 Fe:10 B:2.0 Mna: Bal. | Isitshizi somlilo/ukudibanisa ukungunda kweglasi, ukuphosa okwahlukeneyo kuyafa. |
I-HRNi37A | Igesi atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 35-40HRC | -106+45um -90+45um | C:0.15 IsiKr:4.5 Si:2.6 B:1.2 Mna: Bal. | Isitshizi somlilo/ukudibanisa ukungunda kweglasi, ukuphosa okwahlukeneyo kuyafa. |
I-HRNi45A | Amanzi aneathom | 17-21s / 50g | 3.5-4.5g/cm3 | 42-47HRC | -106+45um -90+45um | C:0.4 Si:3 B:2.6 IKr:12 Fe:5 Mna: Bal. | Isitshizi somlilo / ukudibanisa i-HVOF, umphezulu wokutywina, ipunch, ivalve, ipiston njl. |
I-HRNi50A | Amanzi aneathom | 17-21s / 50g | 3.5-4.5g/cm3 | 45-50HRC | -106+45um -90+45um | C:0.5 Si:3.0 B:3.0 IKr:12 Fe:5 Mna: Bal. | Isitshizi somlilo / ukudibanisa i-HVOF, umphezulu wokutywina, iplunger yeoli kunye neshaft njl. |
I-HRNi55A | Amanzi aneathom | 17-21s / 50g | 3.5-4.5g/cm3 | 52-55HRC | -106+45um -90+45um | C:0.8 Si:4.0 B:3.0 IsiKr:14 Fe:5.0 Mna: Bal. | Isitshizi somlilo/i-fusingHVOF, umphezulu wokutywina, iplunger yeoli kunye neshaft njl. |
I-HRNi60A | Amanzi atomized Gas | 17-21s / 50g | 3.5-4.5g/cm3 | 55-60HRC | -106+45um -90+45um | C:0.9 Si:4.0 B:3.2 IsiKr:16 Fe:5.0 Mna: Bal. | Isitshizi somlilo / ukudibanisa i-HVOF, ukuxhathisa okulungileyo kwe-corrosion, ubunzima obuphezulu, ukunxiba okufanelekileyo kokusebenza, ukukhuhlana okuphantsi. |
HRNi60CuMo | Amanzi aneathom Irhasi i-atom | 17-21s / 50g | 3.5-4.5g/cm3 | 55-60HRC | -106+45um -90+45um | C:0.9 Si:4.0 B:4.0 IsiKr:16 Cu:3.0 Mo:3.0 Fe:5.0 Mna: Bal. | Isitshizi somlilo / ukudibanisa i-HVOF, ukulungisa, i-impeller, ipiston, ivalve njl. |
I-HRNi65A | Amanzi aneathom | 17-21s / 50g | 3.5-4.5g/cm3 | 60-65HRC | -106+45um -90+45um | C:1.1 Si:4.0 B:4.0 IsiKr:18 Fe:5.0 Mna: Bal. | Isitshizi somlilo / i-fusingHVOF, ubunzima obuphezulu kune-Ni60A, i-wire roller, i-plunger, i-conveyor roller njl. |
I-HRNI625 | Amanzi atomized Gas | 17-21s / 50g | 3.5-4.5g/cm3 | 8-15HRC | -106+45um -90+45um -45+15um | C:0.1 Si:0.5 B:0.5 IKr:21 Mo:8.5 Nb:4.0 Fe:5.0 Mnu:0.5 Mna: Bal. | Isitshizi somlilo / ukudibanisa i-HVOF, ukuphumla okulungileyo kokutya kunye nokusebenza okuchasene nobushushu obuphezulu, |
PS: Sikwabonelela ngeenkonzo ezilungiselelwe wena |
1.Ukugubungela umaleko okhethekileyo kwintsimbi kunye neengxenye zetsimbi kunye nezinye iimbumba zeglasi zilungisa.
2.Ukukhusela kwangaphambili kunye nokulungiswa okanye ukomeleza iinxalenye zentengiso.
3.I-FLS/PTA/APS/Laser Cladding application kunye nokudibanisa iNi okanye iNickel base alloy powder layers.
4.Yenza i-coating exinene ngakumbi xa kuthelekiswa ne-FTC, kunye nobunzima obungcono kunye nokudinwa.